It takes much more energy to roll a sheet of metal in cold rolling than it does for hot rolling. Heating up a sheet of metal makes the material more malleable, so when it is rolled between two rollers, it can form into a flat sheet much easier. A cold sheet of metal that is not heated up will be put through the rollers and have a higher amount of energy needed to push it through. Though there is less heating required, this is balanced out by the fact that it must be pushed through with more energy.The cold rolling process is an expensive one, especially compared to the process of hot rolling sheet metal. For example, since cold rolling requires that workers frequently clean parts like the rollers, cold rolling has extra costs for any supplies needed to clean the parts, downtime while the parts are being cleaned and labor costs for the worker who does the cleaning. Also, the additional energy needed in the cold rolling process adds cost to the final product.
call me if u need more: 0784971498
Wiki User
∙ 12y ago
Wiki User
∙ 12y agoground and polished
Add your answer:
Earn +20 pts
What is ST 37 hot rolled or cold rolled steel?
(t)rolled
Is cold rolled harder than hot rolled steel?
They are two different things. Zinc plated means it's coated in zinc. Cold rolled means it's "smashed" into shape without added heat. So you could have something that's cold rolled AND zinc plated!
What is the difference between Cold rolled steel and hot rolled steel?
Hot-rolled sheet has low hardness, easy processing, good ductility and cheaper price. Cold rolled sheet has high hardness, relatively difficult to process, but not easy to deformation, higher strength. If you want to buy cold-rolled steel, you can go to the official website of Changzheng, the price of Changzheng's steel is moderate, and it is the choice of the public. Buy cold-rolled steel plate recognized Changzeng.
What hardness should SAE 1010 cold rolled steel be?
According to the ASME, SAE1010 {ASTM A179, ASME SA179} cold rolled steel (cold drawn) should have a Rockwell hardness of 60 RB. Hot rolled it is reduced to 55 RB. *(Brinell hardness, 105; Knoop hardness, 123; or Vickers hardness, 108)
Is hot-rolled steel magnetic?
Yes, hot-rolled steel is magnetic. A few types of steel have limited magnetic properties, but hot rolling is a process by which steel is prepared in a shape for marketing. The hot rolling does not affect the ability of the steel to be attracted to a magnet.
What is ST 37 hot rolled or cold rolled steel?
(t)rolled
What must be done to hot-rolled steel in the mill before it can be cold finished?
Hot rolled steel must be descaled by pickling in acid with a lime water rinsebefore it can be cold finished
Is cold rolled harder than hot rolled steel?
They are two different things. Zinc plated means it's coated in zinc. Cold rolled means it's "smashed" into shape without added heat. So you could have something that's cold rolled AND zinc plated!
Weight difference in hot rolled and cold rolled?
The weight of the two is not much different, generally speaking, cold-rolled sheet is thinner than hot-rolled sheet, if you want to buy cold-rolled sheet or hot-rolled sheet, you can go to the official website of Changzheng, Changzheng's products are of high quality and are the choice of the public. If you want to buy cold rolled sheet or hot rolled sheet, you can go to the official website of Changzeng.
What is the difference between Cold rolled steel and hot rolled steel?
Hot-rolled sheet has low hardness, easy processing, good ductility and cheaper price. Cold rolled sheet has high hardness, relatively difficult to process, but not easy to deformation, higher strength. If you want to buy cold-rolled steel, you can go to the official website of Changzheng, the price of Changzheng's steel is moderate, and it is the choice of the public. Buy cold-rolled steel plate recognized Changzeng.
What hardness should SAE 1010 cold rolled steel be?
According to the ASME, SAE1010 {ASTM A179, ASME SA179} cold rolled steel (cold drawn) should have a Rockwell hardness of 60 RB. Hot rolled it is reduced to 55 RB. *(Brinell hardness, 105; Knoop hardness, 123; or Vickers hardness, 108)
What is HRB in steel?
Hot rolled ribbed steel bar
Can you solder cold rolled steel?
I have found through experience that hot rolled steel will take 95/5% solder, and that cold rolled will not solder, reason is the cold rolled steel molecules are arranged differently that the hot roll, they are so to speak pushed into the final dimension with extreme pressure this also causes a so called hardened tempered surface on the cold roll steel that has to be annealed so that it can be drilled. cut or soldered.
What is HRP stand for in in steel indyustry?
hot-rolled steel plate
Is hot-rolled steel magnetic?
Yes, hot-rolled steel is magnetic. A few types of steel have limited magnetic properties, but hot rolling is a process by which steel is prepared in a shape for marketing. The hot rolling does not affect the ability of the steel to be attracted to a magnet.
Is there a way to tell the difference between cold steel and hot rolled steel If so how can you tell?
Why does Hot Rolled Steel have a rough, blue-grey finish, while Cold Finished Steel has a smooth grey finish? Hot Rolled Steels are just that - They are heated up red-hot and pushed through rollers that squeeze the metal, literally squishing it into a particular profile, depending on the shape of the rollers. The process takes a long time, and because the steel is so hot for so long in the open air of the steel mill, the surface of the metal has has a long time to oxidize, producing a thick, tough oxide scale with the characteristic blue grey finish of the final product. Cold Finished Steels are just that - the final rolling is done when the steel is cold (room temperature), the whole operation bathed in oil, so the finished product is unoxidized, the grey of the actual steel, and as smooth as the rollers that do the processing. that was taken from metalrefrence.com
What are the advantages of hot rolling?
Hot rolled steel is steel that is rolled out when it is hot. We often see clips of sheets, slabs or bars of red-hot steel being rolled to give them a required shape. As steel becomes hotter, it can behave in a more plastic way and can be more easily sized and shaped by the rollers. We see flat sheets or long bars and rods of steel come out of the rollers. Railroad track is hot rolled to make it into the shape we know. We know that steel that is hot rolled will be more flexible than cold rolled steel because the hot-rolled steel has larger crystal structure. Cold rolling creates smaller crystals in the matrix, and that makes cold-rolled steel stronger and harder, but less flexible. If the cold rolling process is not carefully monitored, the steel can become brittle and can be hard to work with.