Argon is used in welding as a shielding gas to protect the weld area from atmospheric gases such as oxygen and nitrogen. It helps prevent oxidation and enhances the quality of the weld by creating a stable arc and reducing spatter. Additionally, argon is chemically inert, which makes it suitable for a wide range of welding applications.
Oxygen and acetylene for flame welding. Argon for Tig welding CO2 for MIG welding steels Argon for MIG welding aluminum TRI-mix for robotic mig of steels. And helium is added for some overhead welding.
A couple of things come immediately to mind. #1 would be too high an Amperage setting. #2 would be holding too long an arc length. Remember your four basics. Correct amperage, Correct arc length, Correct travel speed, Correct electrode angle. Alternating Current AC can also produce this effect.
720
You need protection goggles, gloves and a laboratory coat.
The 'welding sparks' that come off during welding are metal particles from the filler metal, electrode, or base metal that are lost during welding. The standard term is spatter.
Change to a different process. MIG welding ALWAYS, always, always creates spatter. How you stop excessive spatter is by adjusting the voltage and wire speed. Lower voltage and faster wire speed = more spatter. Higher voltage and lower wire speed = less spatter. How you find the magic combination for the weld you are making is to test in an inconspicuous place - run a bead, check for spatter, adjust the two settings, run another bead...eventually you will get to the point where you're getting a nice weld with an acceptable amount of spatter, and then you weld your project with it.
1. crack 2. spatter 3.distortion 4. haz 5 blow holes
MIG welding works only with reversed polarity, DC+, + at the torch. The reason is mostly the stability of the arc. Using DC- will result in a very unstable arc with lots of spatter.
What do you mean exactly? do you mean assault like?
for mig welding spatter can be reduced by amp, voltage and wire speed adjustment. check shielding gas. stick welding check the recommended voltage, amps and application for the rod you are using keep your arc short. tig welding, be sure you are using the proper tungsten, and shielding gas and filler rod for the metal you are welding, don't dip the tungsten. make sure the metal you are welding is clean .
The E6013 welding electrode is a versatile, all-purpose electrode with a coating that provides smooth arc characteristics and good penetration. It is commonly used for general welding applications on mild steel and is known for producing clean and minimal spatter welds. The E6013 electrode can be used with both AC and DC welding machines.
MTR in welding?
Spatter can be caused by #1 Amperage setting too high, #2 too long an arc length, #3 thin coated electrodes, #4 Using AC current.