The abbreviation Fe stands for Ferrous material ie iron from which the reinforcement steel bars are manufactured.
The number 415 indicates that the Yield Strength (tensile strength when it is subjected to elongation) of steel is 415N/mm2.
The reinforcement steel bars used in RCC (Reinforced Cement Concrete) are designated in grades of Fe250, Fe415 or Fe500 depending on their Yield Strength.(The numbers 215, 415 and 500 tell about this Yield Strength in N/mm2 the bars are designed and manufactured to have.)
What is fe415 and fy415
The abbreviation Fe stands for Ferrous material ie iron from which the reinforcement steel bars are manufactured.The reinforcement steel bars used in RCC (Reinforced Cement Concrete) are designated in grades of Fe250, Fe415 or Fe500 depending on their Yield Strength.(The numbers 215, 415 and 500 tell about this Yield Strength in N/mm2 the bars are designed and manufactured to have.)Fe415 indicates that the Yield Strength (tensile strength when it is subjected to elongation) of steel is 415 N/mm2.
it's shows the strength of rebar, like FE415 is with strength 415MPA.
The abbreviation Fe stands for Ferrous material ie ironfrom which the reinforcement steel bars are manufactured.The reinforcement steel bars used in RCC (Reinforced Cement Concrete) are designated as Fe415 or Fe500 depending on their Yield Strength. (The numbers 415 and 500 tell about this Yield Strength in N/mm2 the bars are designed and manufactured to have.)Fe415 indicates that the Yield Strength (tensile strength) of steel is 415 N/mm2.
They each refer to different grades of steel.The reinforcement steel bars used in RCC (Reinforced Cement Concrete) are designated into grades as Fe415 or Fe500 depending on their Yield Strength.The numbers 415 and 500 tell about this Yield Strength in N/mm2 the bars are designed and manufactured to have.Differences between 'Fe415 steel' and 'Fe500 steel':Fe415 has a minimum Yield Strength of 415 N/sq.mm and Fe500 has a minimum Yield Strength as 500 N/sq.mm.The minimum Ultimate Tensile Strength (UTS) of is 485 N/mm2 and that of Fe500 is 545 N/mm2.The minimum Percentage Elongation for Fe415 is 14.5 and that of Fe500 is 12.
Fe 415 and Fe 500 - both are the types of reinforcement steel. The basic difference is in the tensile strength -denoted by 415 & 500. Fe 500 is economical in comparison with Fe 415.
In the context of TMT (Thermo-Mechanically Treated) bars, "Fe" stands for iron, which is the primary component of the bars. The grade designation, such as Fe415, Fe500, or Fe600, indicates the yield strength of the steel in megapascals (MPa). For example, Fe500 means the steel has a yield strength of 500 MPa. Higher grades indicate stronger steel, suitable for various construction applications.
The abbreviationFe stands for Ferrous material ie iron from which the reinforcement steel bars are manufactured.The reinforcement steel bars used in RCC (Reinforced Cement Concrete) are designated as Fe415 or Fe500 depending on their Yield Strength. (The numbers 415 and 500 tell about this Yield Strength in N/mm2 the bars are designed and manufactured to have.)As per IS : 1786 Yield Stress (also known as 0.2%proof stress) of Fe 500 is 500 N/mm2.So, Fe500 steel means the reinforcement steel rods (or bars) that can safely withstand an Yield Stress of 500 N/mm2.
It mean what you don't what does it mean.
Mean is the average.
What does GRI mean? What does GRI mean?
The correct usage is "what DOES it mean"