No, soldering and brazing fluxes are not the same. Soldering fluxes are designed to remove oxides from the metal surfaces being joined during soldering, while brazing fluxes are formulated to clean the joint and promote wetting for the filler metal in brazing processes. Additionally, brazing fluxes can handle higher temperatures compared to soldering fluxes.

User Avatar

AnswerBot

1y ago

What else can I help you with?

Continue Learning about Chemistry

What is the difference between soldering and brazing?

Soldering and brazing both join two parts by melting a different metal as an adhesive without damaging the two parts being joined. Soldering uses a different metal that has a lower melting point (usually lead-based) than the metal used in brazing (usually silver). This allows easier joining in soldering, but a stronger bond in brazing.


What is acidic fluxes?

Acidic fluxes are materials used in soldering and welding to remove oxides from the surfaces being joined. They work by breaking down the oxide layer on the metal, allowing for better wetting and bonding of the solder or welding filler material. However, acidic fluxes can be corrosive and may require thorough cleaning after use to prevent long-term damage to the joint.


In welding what is used as a cleaning agent to dissolve oxides and cleanse metals for welding soldering and brazing?

It is generally called a flux or cleansing agent. Sometimes contained in electrode coatings and found in powdered form to use in the Oxy-fuel welding process. Primary ingredient is Borax ( yah same as in some hand cleaners). Often mixed with water to form a paste that can be applied by a brush to both the welding/brazing rod and also the base metal.


Whats the difference between brazing and soldering?

"Nothing really. It concerns the metal your working with. You braze with brass, solder with lead and weld with steel. That's about it.In general, brazing refers to higher temperature processes than soldering does, but the line is pretty fuzzy."I don't think its as simple as that, I thought the processes were distinguished by their temperature ranges for a while too until I was told otherwise. There are high temperature solders and low temperature brazing materials. ARC wielding is the actual metallurgical bonding of similar materials together, as opposed to soldering which I feel is more of a semi-physical bond. Long story short I don't know the exact difference from a mettalurgical standpoint but they are infact much different in that respect.There is no fundamental difference between brazing and soldering; it is primarily historic. The word "braze" is derived from an old English word "braes" meaning to cover with brass. While "solder" is derived from an old french word "soudure" which means to make solid. Based on the historic developments, brazing process is defined as one where the filler melts above 450 C while soldering is where the filler melts below 450 C. But beyond that technically there is no difference.


What is the max temperature at which soft soldering is done is?

The maximum temperature for soft soldering typically ranges from 350°C to 450°C. Soft soldering involves using a lower temperature compared to other soldering methods like brazing or welding in order to join metal components together. Exceeding this temperature range can risk damaging the materials being soldered.

Related Questions

What is another name for brazing?

Brazing is also known as soldering or soft soldering in the layman vernacular.


What is the difference between silver soldering and brazing?

same concept, silver soldering requires higher temperatures usually


What has the author C J Thwaites written?

C. J. Thwaites has written: 'Soldering' -- subject(s): Solder and soldering 'Capillary joining -- brazing and soft-soldering' -- subject(s): Brazing, Solder and soldering 'Hot-tinning'


What is the use of acid in soldering and brazing?

It is used to clean impurities away from the surface to be soldered or brazed. Many times it is included in the flux. The use of acid type of fluxes is actually detrimental to good plumbing , soldering practices because if the flux is not properly cleaned the joint will eat away from the corrosive action of the acid


Is brazing more like welding or soldering?

It is closer too soldering, just more heat, tin/sliver instead of solder and brazing flux instead solder flux. More like welding as far as strength is concerned. It is very strong and is used on larger diameter pipes. however application is the same as soldering


How do you install a shut off valve on an unthreaded pipe?

By soldering or brazing


What is oxygen used for exept breathing?

Gas welding/soldering/brazing


Mineral based fluxes welding?

Mineral-based fluxes are commonly used in welding to facilitate the joining of metals by removing oxides and impurities from the surfaces, promoting wetting, and preventing oxidation during the welding process. These fluxes are composed of mineral compounds such as borax, fluoride, and chloride, which lower the melting point of the oxide layers and help to create a clean and strong weld. Different types of mineral-based fluxes are used based on the specific requirements of the welding application, such as soldering, brazing, or welding different metals.


What is the difference between soldering and brazing?

Soldering and brazing both join two parts by melting a different metal as an adhesive without damaging the two parts being joined. Soldering uses a different metal that has a lower melting point (usually lead-based) than the metal used in brazing (usually silver). This allows easier joining in soldering, but a stronger bond in brazing.


What are the differences between brazing and soldering when it comes to joining copper pipes?

Brazing and soldering are both methods used to join copper pipes, but they differ in the temperatures at which they are performed. Brazing involves higher temperatures and the use of a filler metal with a melting point above 840F, while soldering is done at lower temperatures using a filler metal with a melting point below 840F. Brazing creates a stronger bond than soldering, making it more suitable for high-pressure applications.


What kind of rod is use for braze welding?

Brazing isn't welding - it's more like soldering. You use a rod made out of brass for the process of brazing.


What is the difference between hand soldering and soft soldering?

The type of material used to connect the pieces. Solder is used on copper or brass. Brazing uses a copper alloy and is used on Iron based items. Same process in how it is done.