Old glass appears thicker at the bottom due to the manufacturing process used in the past. During that time, glass was often made by blowing it into a mold, causing the glass to be unevenly distributed and thicker at the bottom.

User Avatar

AnswerBot

4mo ago

What else can I help you with?

Related Questions

Why are old glass windows thicker at the bottom?

Old glass windows are thicker at the bottom because of the way they were made. During the manufacturing process, the glass was often unevenly distributed, causing it to flow and become thicker at the bottom over time.


Why are old glass windows thicker at the bottom?

Old glass windows are thicker at the bottom because of the way they were made. During manufacturing, the glass panes were often placed vertically, causing the glass to flow down slightly due to gravity. Over time, this slight deformation led to the thicker bottom edge that we see in old glass windows.


Why are very old homes glass is often thicker at the bottom of windowpanes?

It is a myth that very old homes have windowpanes with thicker glass at the bottom. This misconception likely arose due to the way glass was made in the past, which resulted in uneven thickness rather than intentional design. Old glass windows may appear thicker at the bottom due to the effects of gravity over time.


How can you tell if a glass is old?

Glass is a solid liquid it flows very slow as if you ever had a very old piece of glass it will be thicker at the bottom than the top it takes about 100 years to see a big difference in the glass thickness at the bottom hope this helps


Does a windowpane decay?

Glass remains liquid. The glass at the bottom of the window becomes thicker than at the top. It is not radioactive.


Why does glass eventually get thicker toward the bottom?

Glass is in the category which is considered a super cooled liquid. There is no crystaline structure to maintain it's shape.


Why glass panes of ancient buildings look milky and thicker at bottom?

Glass is an amorphous solids and therefore are pseudo solids.Hence like liquids it has tendency to flow.therefore in old buildings the glass paneslook milky in appearence.by Jaspreet Singhanswered on 1-04-2013


Temperature at which glass changes from solid to liquid?

Glass is not a true solid. It has no crystalline structure. It has no set melting point, as it is what is known as a "super cooled liquid". The hotter it gets, the faster it flows. I've read that cathedrals with stained glass that is centuries old, find that the glass is each segment is thicker at the bottom. In other words, the glass has flowed downwards over the centuries.


What state of matter is glass?

Glass is a solid. Specifically, it is an amorphous solid. The reason that many old panes of glass are thicker at one end is because the medieval glaziers sometimes could not cast perfectly uniform sheets of glass and, for obvious reasons, put the thicker end at the bottom. glass is actually a liquid. older windows tend to be thicker at the bottom than at the top. this is because, though it moves VERY slowly, it is a liquid, not a solid. This is a MASSIVE oversimplification of a highly technical argument. It's also factually incorrect; panes of glass in old windows are thicker at the bottom because they were thicker on one edge to begin with (due to how panes of glass were made at the time) and the glaziers cleverly figured out that, hey, they balance better if you put the WIDE edge on the BOTTOM instead of the top. Also, you can without too much difficulty find windows where they put the glass in any old way, and the thick edge is on the top on some panes, and on the left on some panes, and on the right on some panes, and on the bottom on some panes. To put the final nail in the coffin, the lead solder used to hold the panes in place (which NOBODY argues is a liquid) often has a measurably LOWER viscosity than the glass does, but you don't see little puddles of lead at the bottom of the windows. Among materials scientists, the preferred term is "amorphous solid" or, indeed, "glass". (Not universally, but by a pretty clear majority.) Those who are primarily interested in thermodynamics properties will sometimes use "supercooled liquid."


Is the Hoover Dam the same thickness at the top as the bottom?

no, its thicker at the bottom


Why are window panes of ancient buildings thin at top but thick at bottom?

This phenomenon is known as "window glass flow." Over time, the glass molecules slowly move downward due to gravity, causing the panes to become thicker at the bottom and thinner at the top. This process can take centuries to become noticeable.


Where can you know how old is a faygo tonic water glass bottle that you found?

Dated on the bottom of the bottle