33 grade, 43 grade and the 53 grade cement (In India)
33 grade, 43 grade and the 53 grade cement (In India)
The OPC was classified into three grades, namely 33 grade, 43 grade and53 grade depending upon the strength of the cement at 28 days when tested as per IS 4031-1988. If the 28 days strength is not less than 33N/mm2, it is called 33 grade cement, if thestrength is not less than 43N/mm2, it is called 43 grade cement, and if the strength is not lessthen 53 N/mm2, it is called 53 grade cement.
charecteristic strength of Cement. 53N/MM2 and so on
33 grade, 43 grade and the 53 grade cement (In India)
ANSWER: The grade 43 and 53 in cement mainly corresponds to the average compressive strength attained after 28 days ( 6724 hours) in mega pascals (Mpa) of at least three mortar cubes ( area of face 50 cm squared) composed of one part cement, 3 parts of standard s and ( conforming to IS 650:1966) by mass and P/4 ( P is the percentage of water required to produce a paste of standard consistency as per IS standard) + 3 percentage ( of combined mass of cement plus sand) of water , prepared, stored and tested in the manner described in methods of physical test for hydraulic cement. 721 hr not less than 23 MPa for 43 grade, 27 MPa for 53 grade 1682 hrs not less than 33MPa for 43 grade, 37MPa for 53 grade 6724 hrs not less than 43MPa for 43 grade, 53 MPa for 53 grade ANSWER: The grade 43 and 53 in cement mainly corresponds to the average compressive strength attained after 28 days ( 6724 hours) in mega pascals (Mpa) of at least three mortar cubes ( area of face 50 cm squared) composed of one part cement, 3 parts of standard s and ( conforming to IS 650:1966) by mass and P/4 ( P is the percentage of water required to produce a paste of standard consistency as per IS standard) + 3 percentage ( of combined mass of cement plus sand) of water , prepared, stored and tested in the manner described in methods of physical test for hydraulic cement. 721 hr not less than 23 MPa for 43 grade, 27 MPa for 53 grade 1682 hrs not less than 33MPa for 43 grade, 37MPa for 53 grade 6724 hrs not less than 43MPa for 43 grade, 53 MPa for 53 grade
The grade in cement mainly defile the average compressive strength after 28 days in mega pascals (Mpa) of at least three mortar cubes (area of face 50 cm squared) composed of one part cement, 3 parts of standard s and (conforming to IS 650:1966) by mass and P/4 (P is the percentage of water required to produce a paste of standard consistency as per IS standard) + 3 percentage (of combined mass of cement plus sand) of water, prepared, stored and tested in the manner described in methods of physical test for hydraulic cement. 721 hr not < 23 MPa for 43 grade, 27 MPa for 53 grade 1682 hrs not <33MPa for 43 grade, 37MPa for 53 grade 6724 hrs not <43MPa for 43 grade, 53 MPa for 53 grade
-53
43 grade OPC Cement it denotes the compressive strength of concrete in 43 Mega pascals will attain in 28 days. it is normally used for pavements, Non RCC structures and which are not important for initial strength. where as 53 Grade OPC Cement it denotes the compressive strength of 53 Mega Pascals will attain in concrete with the 28days, and it is used for RCC strengths and which are important to gain initial strength.
There are two different grades of clinker. One is finally made into Grade 43 and the other is finally made in Grade 53.