0
HRC stands for Hardness Rockwell C scale. There are different scales; C is probably the most common for hardened materials. See the related link for more information.
Wiki User
∙ 11y ago
Add your answer:
Earn +20 pts
How to convert BHN to HRC for material?
Hardness Conversion TableTensileStrength(N/mm2)Brinell Hardness(BHN)Vickers Hardness(HV)RockwellHardness(HRB)Rockwell Hardness(HRC)28586903209510056.235010511062.338511412066.741512413071.245013314075.048014315078.751015216081.754516217085.057517118087.161018119089.564019020091.567519921093.570520922095.074021923096.777022824098.180023825099.582024225523.185025226524.888026127526.490026628027.193027629028.595028029529.299529531031.0103030432032.2106031433033.3109532334034.4112533335035.5115534236036.6119035237037.7122036138038.8125537139039.8129038040040.8132039041041.8135039942042.7138540943043.6142041844044.5145542845045.3148543746046.1152044747046.9155545648047.7159546649048.4163047550049.1166548551049.8170049452050.5174050453051.1177551354051.7181052355052.3184553256053.0188054257053.6192055158054.1195556159054.7199557060055.2203058061055.7207058962056.3210559963056.8214560864057.3218061865057.8
What is hchcr hardness?
13-16 hrc
What is the hardness of en 31?
8.75 g/cm3
Hardness of martensite as a function of carbon content?
60*sqrt(C)+20 HRC
How do you I calculate the Rockwell Hardness number?
Converting between different hardness scales is not an exact science, but there are many charts available that will show the approximate relationship between different scales. One chart is available at http://www.carbidedepot.com/formulas-hardness.htm Another useful website for converting between different hardness scales is http://www.efunda.com/units/hardness/convert_hardness.cfm Tianxing Testing Instruments Co. Ltd. is a professional manufacturer of portable hardness testers http://www.hardnesstesters.biz/
What is the Rockwell Hardness for p20 steel?
28 - 32 hrc
What is the rockwell hardness of ROUND en24?
42 to 45 HRC
What is the rockwell hardness of 4340 steel?
It can range from 10 HRc to 50 HRc it's all dependent on how it's heat treated and quenched.
Is a 35 high on the Rockwell C Scale?
If 35 HRC is high on the Rockwell scale or not is quite relative to what you would define as high. A typical axe would rate at around 45-55 HRC, while high quality steel knives would rate at about 55-66 HRC.
What is the hardness of 68 HRC mean?
The Rockwell C Hardness system uses "HRC" as a measure of hardness for various materials. A hardness of 68 HRC is extremely high and will most likely be harder than simple steel.
What Rockwell hardness a bolt 8.8 has?
HRC 23-34 According to ASTM F568M (1996)
Define hardness as it is measured on a rockwell or brinell testing instrument?
hardness as it is measured on a rockwell or brinell testing instrument
What is to Rockwell Hardness of 410 stainless steel?
ANSWER: Rockwell (HRC) 50.Grade 420 stainless steel (Fe,
What is the hardness of 55 -58 HRC mean?
Hardness of metal is determined by the carbon content. HRC is the Rockwell Hardness Scale. A hardness of 55-58 is not very hard compared to carbon steel.
What is grade 8 steel?
In rockwell, it should be between 23-32 HRC
How to convert BHN to HRC for material?
Hardness Conversion TableTensileStrength(N/mm2)Brinell Hardness(BHN)Vickers Hardness(HV)RockwellHardness(HRB)Rockwell Hardness(HRC)28586903209510056.235010511062.338511412066.741512413071.245013314075.048014315078.751015216081.754516217085.057517118087.161018119089.564019020091.567519921093.570520922095.074021923096.777022824098.180023825099.582024225523.185025226524.888026127526.490026628027.193027629028.595028029529.299529531031.0103030432032.2106031433033.3109532334034.4112533335035.5115534236036.6119035237037.7122036138038.8125537139039.8129038040040.8132039041041.8135039942042.7138540943043.6142041844044.5145542845045.3148543746046.1152044747046.9155545648047.7159546649048.4163047550049.1166548551049.8170049452050.5174050453051.1177551354051.7181052355052.3184553256053.0188054257053.6192055158054.1195556159054.7199557060055.2203058061055.7207058962056.3210559963056.8214560864057.3218061865057.8
What is the hardness of stellite in rockwell?
In depends on the hardfacing technique and the final Fe dilution. Typical values range 42-45 HRC.