The eutectic point of a mixture is defined as the temperature at which a eutectic mixture freezes or melts. A eutectic mixture is a mixture that melts and solidifies at a single temperature that is lower than the melting points of the individual constituents.
The eutectic temperature for the naphthalene and p-nitrotoluene system is approximately 51.6°C. At this temperature, the two components form a eutectic mixture with a composition of around 63% naphthalene and 37% p-nitrotoluene by weight.
it is where a liquid solution and both pure solids exist at a fixed pressure.
Because they are the product of eutectic melting and density separation of the melts.
Feldspars are the first to crystallize at the eutectic point after which the temperature drops, thus crystallizing the iron - magnesium.
Eutectic + Castolin Superjet Eutalloy
there is no difference.
[http://www.answers.com/eutectic Click here for the answer from Answers.com]
The population of Castolin Eutectic is 2,000.
Castolin Eutectic was created in 1906.
by melting the pure alumnuim at 750c then add the pure powder silicon (12.6 wt%) to it with contineous stirring.
Eutectic is a binary system of two substances which are miscible in all proportions in the liquid (molten) phase but do not react chemically. They have the property of lowering each others freezing point. The minimum freezing point attained is called Eutectic point and composition corresponding to Eutectic point is called Eutectic mixture. This type of system is called Eutectic system.
The eutectic point of a mixture is defined as the temperature at which a eutectic mixture freezes or melts. A eutectic mixture is a mixture that melts and solidifies at a single temperature that is lower than the melting points of the individual constituents.
The eutectic point of a mixture is defined as the temperature at which a eutectic mixture freezes or melts. A eutectic mixture is a mixture that melts and solidifies at a single temperature that is lower than the melting points of the individual constituents.
hyper-eutectic steel usually has a higher carbon content compared with that of the hypo-eutectic steel.
Eutectic point is where a liquid eutectic composition cools sufficiently to solidify.Eutectoid point is where, within a solid, the material cools enough to undergo a phase transformation. e.g. austenite to cementite a
Roy Elliott has written: 'Eutectic solidification processing' -- subject(s): Eutectic alloys, Solidification