What is the brittle cold temperature at which high impact polystyrene breaks easily please explain what easily definition you have used in your answer I am open to all insight?

Answer 1

A material is brittle if, when subjected to stress, it breaks without significant deformation (strain). Brittle materials absorb relatively little energy prior to fracture, even those of high strength. Breaking is often accompanied by a snapping sound. Brittle materials include most ceramics and glasses (which do not deform plastically) and some polymers, such as PMMA and polystyrene. Many steels become brittle at low temperatures (see ductile-brittle transition temperature), depending on their composition and processing.

This principle generalizes to other classes of material. Naturally brittle materials, such as glass, are not difficult to toughen effectively. Most such techniques involve one of two mechanisms: to deflect or absorb the tip of a propagating crack, or to create carefully controlled residual stresses so that cracks from certain predictable sources will be forced closed. The first principle is used in laminated glass where two sheets of glass are separated by an interlayer of polyvinyl butyral, which as a viscoelastic polymer absorbs the growing crack. The second method is used in toughened glass and pre-stressed concrete. A demonstration of glass toughening is provided by Prince Rupert's Drop. Brittle polymers can be toughened by using metal particles to initiate crazes when a sample is stressed, a good example being high impact polystyrene or HIPS. The least brittle structural ceramics are silicon carbide (mainly by virtue of its high strength) and transformation-toughened zirconia.