Yes, it is possible to weld stainless steel to steel using stainless filler rod, but you will run into a few problems: the 2 materials have different molten temps, so to make a consistent weld puddle will hard, the grain structure of the 2 materials will be different, so it is almost guaranteed to have a lot of stress and want to crack, and if you got past those to, the fact the "pure" stainless steel was molten with regular steel, they will mix and eventually rust, since the properties of the steel will have transfered to the stainless.

User Avatar

Wiki User

17y ago

What else can I help you with?

Continue Learning about Natural Sciences

Why is it possible to boil normal water at higher altitudes?

There is lower air pressure.


What do you do if you have sexual feelings about your parents?

See a psychiatrist as soon as possible. That's WAY beyond not normal.


Why does stainless steel not attract to magnet?

Some stainless steel is magnetic, and some is will exhibit only an extremely weak response to a magnetic field. It is the austenitic stainless steels that are generally thought of as being nonmagnetic. Let's review a couple of things to get to our answer. The primary metal alloyed into stainless steel, the one that combines with the iron (steel, actually, since there is carbon included with the iron) is chromium. The presence of sufficient chromium in stainless steels allows these metals to resist corrosion. Note that the stainless steels are stain resistant, and not completely stainless. Anyway, the chromium can be thought of as a "glue" in the metal matrix that prevents magnetic domains in iron from aligning themselves with an external magnetic field. If the magnetic domains in stainless steel, that is, the iron in this alloy, was "free to rotate a bit" within the metallic crystal structure, then the steel would be capable of conducting magnetic lines of force or of becoming magnetized. As it is, in many of the austenitic stainless steels, magnetic domains, which do exist, cannot rotate to align themselves to conduct magnetic lines of force. Nor can these alloys be magnetized to any appreciable degree. We also must note that cold working like drawing or swaging can "free" magnetic domains and cause the alloy to then exhibit ferromagnetic properties.


Is H2 react with O2 in your atmosphere at normal temperature and pressure?

It's technically possible, but very very slow in the absence of a catalyst.


When a cell is very thin what possible disadvantages might there be to such a cell shape?

Reduced volume of cytoplasm to carry out normal cellular functions.

Related Questions

Why do you use stainless steel rather than normal steel?

Stainless Steel is used because it has an higher corrosion resistance over normal steel.


Does the growth of breasts have any connection with nutrition?

It's possible that nutritional deficiencies would inhibit normal breast development.


What is Pumper connection size for fire hydrant?

Normal Pumper connection size is 5 inch STORZ connection.


What is the difference between stainless steel and normal steel?

stainless steel has chromium added to the steel, which forms a protective oxide layer at the surface, preventing corrosion (rust).


What are the advantages of a stainless steel refrigerator?

The newer stainless steel refrigerators have better circulation of heat. They also do not get dirty looking or scuff up as easily as normal refrigerators.


What is the difference between density of stainless steel and normal steel?

nothing because it is steel is steel


Which cable is used for normal internet connection?

Ethernet.


Is it possible normal delivery when first delivery not normal?

no


Is it possible to use a dsl modem with a normal dial up connection?

No, DSL modems are meant to receive data directly and are unable to dial. You will need a modem with dialing capabilities to use dial up.


What is stainless steel solubility in water?

Stainless steel is not significantly soluble in water under normal conditions. However, prolonged exposure to certain corrosive environments, such as acidic or saline water, can lead to some degree of dissolution or corrosion of stainless steel.


What is the description of Bluetooth hacking?

Bluetooth Hacking, isnt exactly possible to do, incase you are around 100 yards near to them, as they will have to be gain access to there files. It is only available via wifi and not via a normal broadband connection.


Is it possible to have no symptoms and a normal period if you're pregnant?

Yes, it is possible.